| 1.- CABLE CONSTRUCTION | |||
| Inner conductor | Copper covered steel wire min. 21% | 1,02+/- 0,01 | |
| Elongation at break | min 1% | ||
| Tensile strength | min. 380 N/mm2 | ||
| Adherence to dielectric | min. 22 N | ||
| Dielectric | Gas injected foamed polyethylene | 4,60 +/- 0,1 | |
| Shrinkage max 4 % after 4 hours at 115 ºC | |||
| Dielectric constant of base PE 2,25 | |||
| Dielectric strength 1of PE 18 kV/mm | |||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | ||
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | ||
| First screen | Tape Aluminium/Polyester/Aluminium | 4,78 +/- 0,13 | |
| dielectric - Ovality | max. 0,33 | ||
| Tape thickness0.009AL/0.012Pet/0.009AL | |||
| Overlapping | min 18% | ||
| Second screen | Aluminum alloy braid | 5,38 +/- 0,15 | |
| Type 5154A or (5056, 5154, 5954) | |||
| Braid construction 16 x 5 x (0,12+0,01/-0,01) | min. 60% | ||
| Elongation at break for every wire | min 3% | ||
| Tensile strength for every wire | 300N/mm2 | ||
| Sheath | PVC - NO BAD ODORS | 6,80 +/-0.15 | |
| Sheath color WHITE | Thickness 0,80+/-0.10 mm | ||
| Jacket thickness excentricity | max. 43 % | ||
| Tensile strength | min .11MPa(TM2) | ||
| Tensile strength after 168 H at 80 ºc | +/- 20% (TM2) | ||
| Elongation at break | min. 150 %(TM2) | ||
| Elongation at break after 168 H at 80 ºC | +/- 20% (TM2) | ||
| Spark test | min. 2,5 kVrms | ||
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | ||
| 2. Cable environmental characteristics | ||||
| Environmental Space | Indoor | Outdoor | |||
| Working temperature | -20 ºC +75 ºC | |||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | ||
| Flame Test Listing | vertical flame | IEC 60332-1-2 | ||
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | ||
| 3- ELECTRICAL CHARACTERISTICS | ||||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | ||||
| Inner conductor resistance | Ohmios /km max. 102 | |||
| Outer conductor resistance | Ohmios /km max. 37 | |||
| Max. Loop current | Ampers 8 a 20 ºC - 6 a 40 ºC | |||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | |||
| Insulation resistance | Mohm x km > 10000 Mohm x km | |||
| Mutual capacitance | 53±2nF/km | |||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | |||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | ||||
| Velocity of propagation | % | 84±2 | ||
| Characteristic impedance | Ohmios | 75 +/- 3 | ||
| Nominal Delay | nS/m max. | 4,0 | ||
| Transfer Impedance | 5-30MHz | ≤50mOhm/m | IEC62153-4-3 | |
| Shielding Effectiveness | 30-1000MHz | ≥75dB | IEC62153-4-4 | |
| 1000-2000MHz | ≥65dB | |||
| 2000-3000MHz | ≥55dB | |||
| Longitudinal attenuation | MHz | dB/100m MAX | ||
| 10 | 2.46 | |||
| 50 | 4.86 | |||
| 100 | 6.56 | |||
| 230 | 10.73 | |||
| 300 | 11.65 | |||
| 400 | 13.62 | |||
| 470 | 14.78 | |||
| 800 | 21.00 | |||
| 860 | 20.05 | |||
| 1000 | 21.49 | |||
| 1350 | 24.71 | |||
| 1750 | 28.67 | |||
| 2150 | 31.79 | |||
| 3000 | 37.53 | |||
| Return Loss | 5 MHz - 470MHz | ≥20dB | ||
| 470 MHz - 1000MHz | ≥18dB | |||
| 1000 MHz - 2000MHz | ≥16dB | |||
| 2000 MHz - 3000MHz | ≥15dB | |||
| 1.- CABLE CONSTRUCTION | |||
| Inner conductor | Bare Copper | 0,80+/- 0,01 | |
| Elongation at break | min 20% | ||
| Adherence to dielectric | 22 -89 N | ||
| Dielectric | Gas injected foamed polyethylene | 3,50 +/- 0,1 | |
| Shrinkage max 4 % after 4 hours at 115 ºC | |||
| Dielectric constant of base PE 2,25 | |||
| Dielectric strength 1of PE 18 kV/mm | |||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | ||
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | ||
| First screen | Tape Aluminium/Polyester/Aluminium | 3,73 +/- 0,13 | |
| dielectric - Ovality | max. 0,28 | ||
| Tape thickness0.009AL/0.012Pet/0.009A | |||
| Overlapping | min 18% | ||
| Second screen | CUSN braid | 4,10 +/- 0,15 | |
| Braid construction 52 x (0,10+0,01/-0,01) | min. 40% | ||
| Elongation at break for every wire | min 20% | ||
| Tensile strength for every wire | 150N/mm2 | ||
| Sheath | PVC - NO BAD ODORS | 5,00 +/-0.15 | |
| Sheath color WHITE | Thickness 0,50+/-0.05 mm | ||
| Jacket thickness excentricity | max. 43 % | ||
| Tensile strength | min .11MPa(TM2) | ||
| Tensile strength after 168 H at 80 ºc | +/- 20%(TM2) | ||
| Elongation at break | min. 150 %(TM2) | ||
| Elongation at break after 168 H at 80 ºC | +/- 20%(TM2) | ||
| Spark test | min. 2,5 kVrms | ||
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | ||
| 2. Cable environmental characteristics | ||||
| Environmental Space | Indoor | Outdoor | |||
| Working temperature | -20 ºC +75 ºC | |||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | ||
| Flame Test Listing | vertical flame | IEC 60332-1-2 | ||
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | ||
| 3- ELECTRICAL CHARACTERISTICS | ||||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | ||||
| Inner conductor resistance | Ohmios /km max. 37 | |||
| Outer conductor resistance | Ohmios /km max. 35 | |||
| Max. Loop current | Ampers 8 a 20 ºC - 6 a 40 ºC | |||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | |||
| Insulation resistance | Mohm x km > 10000 Mohm x km | |||
| Mutual capacitance | 53±2nF/km | |||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | |||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | ||||
| Velocity of propagation | % | 84±2 | ||
| Characteristic impedance | Ohmios | 75 +/- 3 | ||
| Nominal Delay | nS/m max. | 4,0 | ||
| Transfer Impedance | 5-30MHz | ≤50mOhm/m | IEC62153-4-3 | |
| Shielding Effectiveness | 30-1000MHz | ≥75dB | IEC62153-4-4 | |
| 1000-2000MHz | ≥65dB | |||
| 2000-3000MHz | ≥55dB | |||
| Longitudinal attenuation | MHz | dB/100m MAX | ||
| 10 | 3.0 | |||
| 50 | 6.1 | |||
| 100 | 8.0 | |||
| 230 | 12.3 | |||
| 300 | 14.2 | |||
| 400 | 16.5 | |||
| 470 | 18.5 | |||
| 800 | 23.0 | |||
| 860 | 25.5 | |||
| 1000 | 26.8 | |||
| 1350 | 31.5 | |||
| 1750 | 36.4 | |||
| 2150 | 40.3 | |||
| 3000 | 48.0 | |||
| Return Loss | 5 MHz - 470MHz | ≥20dB | ||
| 470 MHz - 1000MHz | ≥18dB | |||
| 1000 MHz - 2000MHz | ≥16dB | |||
| 2000 MHz - 3000MHz | ≥15dB | |||
| 1.- CABLE CONSTRUCTION | ||
| Inner conductor | Bare Copper | 7*0.20 +/-0.01 |
| Elongation at break | min 20% | |
| Adherence to dielectric | 22 -89 N | |
| Dielectric | polyethylene | 3.70 +/-0.05 |
| Dielectric constant of base PE 2,25 | ||
| Dielectric strength 1of PE 18 kV/mm | ||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | |
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | |
| First screen | Copper Clad Aluminium Wire Braid | 4,05 +/- 0,15 |
| Braid construction 16 x 7x (0,12+0,003/-0,003) | min. 84% | |
| Elongation at break for every wire | min 6% | |
| Tensile strength for every wire | 190N/mm2 | |
| Sheath | PVC - NO BAD ODORS | 6.15 +/-0.20 |
| Sheath color BLACK RAL 9005 | Thickness 0,8±0.1 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa（TM2） | |
| Tensile strength after 168 H at 80 ºc | +/-20% （TM2） | |
| Elongation at break | min. 150 %（TM2） | |
| Elongation at break after 168 H at 80 ºC | +/-20%（TM2） | |
| Bending test at low temperature | -15°C | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| Sheath marking | ||
| Delivery form | ||
| 2. Cable environmental characteristics | |||
| Environmental Space | Indoor | Outdoor | ||
| Working temperature | -20 ºC +75 ºC | ||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | |
| Flame Test Listing | vertical flame | IEC 60332-1-2 | |
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | |
| 3.- ELECTRICAL CHARACTERISTICS | |||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | |||
| Inner conductor resistance | Ohmios /km max. 65 | ||
| Outer conductor resistance | Ohmios /km max. 42 | ||
| Max. Loop current | Ampers 8 a 20 ºC - 5 a 40 ºC | ||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | ||
| Insulation resistance | Mohm x km > 5000 Mohm x km | ||
| Mutual capacitance | 67±2nF/km | ||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | ||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | |||
| Velocity of propagation | % | 66 | |
| Characteristic impedance | Ohmios | 75 +/- 3 | |
| Nominal Delay | nS/m max. | 5,1 | |
| MHz | dB/100m NOM | ||
| 50 | 8.5 | ||
| 100 | 11.8 | ||
| 200 | 16.5 | ||
| 450 | 26 | ||
| 800 | 35.8 | ||
| 800 | 35.8 | ||
| 1000 | 39.5 | ||
| Return Loss | 5 MHz - 1000 MHz | min. 20dB | |
| 1.- CABLE CONSTRUCTION | ||
| Inner conductor | Bare Copper | 7*0.20 +/-0.01 |
| Elongation at break | min 20% | |
| Adherence to dielectric | 22 -89 N | |
| Dielectric | polyethylene | 3.70 +/-0.05 |
| Dielectric constant of base PE 2,25 | ||
| Dielectric strength 1of PE 18 kV/mm | ||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | |
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | |
| First screen | Copper Clad Aluminium Wire Braid | 4,05 +/- 0,15 |
| Braid construction 16 x 7x (0,12+0,003/-0,003) | min. 84% | |
| Elongation at break for every wire | min 6% | |
| Tensile strength for every wire | 190N/mm2 | |
| Inner Sheath | PVC - NO BAD ODORS | 6.15 +/-0.20 |
| Sheath color BLACK RAL 9005 | Thickness 0,8±0.1 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa （TM2） | |
| Tensile strength after 168 H at 80 ºc | +/-20% （TM2） | |
| Elongation at break | min. 150 %（TM2） | |
| Elongation at break after 168 H at 80 ºC | +/-20% （TM2） | |
| Bending test at low temperature | -15°C | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| Power cord | Bare Copper 24*0.20±0.02mm+1.80mm PVC BLACK | 0.75mm2 |
| Bare Copper 24*0.20±0.01mm+ 1.80mm PVC RED | 0.75mm2 | |
| Outer Sheath | PVC - NO BAD ODORS | 10.0 +/-0.30 |
| Sheath color BLACK RAL 9005 | Thickness 1,0±0.2 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa （TM2） | |
| Tensile strength after 168 H at 80 ºc | +/-20%（TM2） | |
| Elongation at break | min. 150 %（TM2） | |
| Elongation at break after 168 H at 80 ºC | +/-20% （TM2） | |
| Bending test at low temperature | -15°C | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| 2. Cable environmental characteristics | |||
| Environmental Space | Indoor | Outdoor | ||
| Working temperature | -20 ºC +75 ºC | ||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | |
| Flame Test Listing | vertical flame | IEC 60332-1-2 | |
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | |
| 3.- ELECTRICAL CHARACTERISTICS | |||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | |||
| Inner conductor resistance | Ohmios /km max. 65 | ||
| Outer conductor resistance | Ohmios /km max. 42 | ||
| Max. Loop current | Ampers 8 a 20 ºC - 5 a 40 ºC | ||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | ||
| Insulation resistance | Mohm x km > 5000 Mohm x km | ||
| Mutual capacitance | 67±2nF/km | ||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | ||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | |||
| Velocity of propagation | % | 66 | |
| Characteristic impedance | Ohmios | 75 +/- 3 | |
| Nominal Delay | nS/m max. | 5,1 | |
| MHz | dB/100m NOM | ||
| 50 | 8.5 | ||
| 100 | 11.8 | ||
| 200 | 16.5 | ||
| 450 | 26 | ||
| 800 | 35.8 | ||
| 800 | 35.8 | ||
| 1000 | 39.5 | ||
| Return Loss | 5 MHz - 1000 MHz | min. 20dB | |
| 1.- CABLE CONSTRUCTION | ||
| Inner conductor | Bare Copper | 7*0.20 +/-0.01 |
| Elongation at break | min 20% | |
| Adherence to dielectric | 22 -89 N | |
| Dielectric | polyethylene | 3.70 +/-0.05 |
| Dielectric constant of base PE 2,25 | ||
| Dielectric strength 1of PE 18 kV/mm | ||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | |
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | |
| First screen | Copper Clad Aluminium Wire Braid | 4,05 +/- 0,15 |
| Braid construction 16 x 7x (0,12+0,003/-0,003) | min. 84% | |
| Elongation at break for every wire | min 6% | |
| Tensile strength for every wire | 190N/mm2 | |
| Power cord | Bare Copper 24*0.20±0.02mm+1.80mm PVC BLACK | 0.75mm2 |
| Bare Copper 24*0.20±0.01mm+ 1.80mm PVC RED | 0.75mm2 | |
| Power cord Out Sheath | PVC - NO BAD ODORS | 4.80±3.0mm |
| Sheath color GREEN RAL 6026 | Thickness min. 0,5mm | |
| Jacket thickness excentricity | max. 43 % | |
| Sheath | PVC - NO BAD ODORS | 6.15 +/-0.20 |
| Sheath color GREEN RAL 6026 | Thickness 0,8±0.1 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa （TM2） | |
| Tensile strength after 168 H at 80 ºc | +/-20% （TM2） | |
| Elongation at break | min. 150 %（TM2） | |
| Elongation at break after 168 H at 80 ºC | +/-20%（TM2） | |
| Bending test at low temperature | -15°C | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| 2. Cable environmental characteristics | |||
| Environmental Space | Indoor | Outdoor | ||
| Working temperature | -20 ºC +75 ºC | ||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | |
| Flame Test Listing | vertical flame | IEC 60332-1-2 | |
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | |
| 3.- ELECTRICAL CHARACTERISTICS | |||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | |||
| Inner conductor resistance | Ohmios /km max. 65 | ||
| Outer conductor resistance | Ohmios /km max. 42 | ||
| Max. Loop current | Ampers 8 a 20 ºC - 5 a 40 ºC | ||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | ||
| Insulation resistance | Mohm x km > 5000 Mohm x km | ||
| Mutual capacitance | 67±2nF/km | ||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | ||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | |||
| Velocity of propagation | % | 66 | |
| Characteristic impedance | Ohmios | 75 +/- 3 | |
| Nominal Delay | nS/m max. | 5,1 | |
| MHz | dB/100m NOM | ||
| 50 | 8.5 | ||
| 100 | 11.8 | ||
| 200 | 16.5 | ||
| 450 | 26 | ||
| 800 | 35.8 | ||
| 800 | 35.8 | ||
| 1000 | 39.5 | ||
| Return Loss | 5 MHz - 1000 MHz | min. 20dB | |
| 1.- CABLE CONSTRUCTION | ||
| Inner conductor | Bare Copper | 7*0.40+/- 0,01 |
| Elongation at break | min 25% | |
| Adherence to dielectric | min. 22 N | |
| Dielectric | Gas injected foamed polyethylene | 4,90 +/- 0,1 |
| Shrinkage max 4 % after 4 hours at 115 ºC | ||
| Dielectric constant of base PE 2,25 | ||
| Dielectric strength 1of PE 18 kV/mm | ||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | |
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | |
| First screen | Tape Aluminium/Polyester/Aluminium + bonding layer | 5,10 +/- 0,13 |
| dielectric - Ovality | max. 0,33 | |
| Tape thickness0.009AL/0.012Pet/0.009AL/0.025EAA | ||
| Overlapping | min 18% | |
| Second screen | Annealed Tinned copper | 5,38 +/- 0,15 |
| Braid construction 16 x 9 x (0,12+0,01/-0,01) | min. 90% | |
| Elongation at break for every wire | min 25% | |
| Tensile strength for every wire | 180N/mm2 | |
| Sheath | PVC - NO BAD ODORS | 7,00 +/-0.15 |
| Sheath color BLUE | Thickness 0,80+/-0.10 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa (TM2) | |
| Tensile strength after 168 H at 80 ºc | +/- 20% (TM2) | |
| Elongation at break | min. 150 % (TM2) | |
| Elongation at break after 168 H at 80 ºC | +/- 20%(TM2) | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| 2. Cable environmental characteristics | ||
| Environmental Space | Indoor | Outdoor | |
| Working temperature | -20 ºC +75 ºC | |
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 |
| Flame Test Listing | vertical flame | IEC 60332-1-2 |
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 |
| 3- ELECTRICAL CHARACTERISTICS | ||||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | ||||
| Inner conductor resistance | Ohmios /km max. 19.7 | |||
| Outer conductor resistance | Ohmios /km max. 11 | |||
| Max. Loop current | Ampers 8 a 20 ºC - 6 a 40 ºC | |||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | |||
| Insulation resistance | Mohm x km > 10000 Mohm x km | |||
| Mutual capacitance | 53±2nF/km | |||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | |||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | ||||
| Velocity of propagation | % | 84±2 | ||
| Characteristic impedance | Ohmios | 75 +/- 3 | ||
| Nominal Delay | nS/m max. | 4,0 | ||
| Transfer Impedance | 5-30MHz | ≤5mOhm/m | IEC62153-4-3 | |
| Shielding Effectiveness | 30-1000MHz | ≥85dB | IEC62153-4-4 | |
| 1000-2000MHz | ≥75dB | |||
| 2000-3000MHz | ≥65dB | |||
| Longitudinal attenuation | MHz | dB/100m MAX | ||
| 5 | 1.60 | |||
| 10 | 2.21 | |||
| 50 | 4.60 | |||
| 100 | 6.40 | |||
| 200 | 9.30 | |||
| 500 | 15.40 | |||
| 800 | 20.50 | |||
| 1000 | 23.50 | |||
| Return Loss | 5 MHz - 470MHz | ≥20dB | ||
| 470 MHz - 1000MHz | ≥18dB | |||
| 1.- CABLE CONSTRUCTION | ||
| Inner conductor | Bare Copper | 0,58+/- 0,01 |
| Elongation at break | min 20% | |
| Adherence to dielectric | 22 -89 N | |
| Dielectric | polyethylene | 3.70 +/-0.05 |
| Dielectric constant of base PE 2,25 | ||
| Dielectric strength 1of PE 18 kV/mm | ||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | |
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | |
| First screen | Copper Clad Aluminium Wire Braid | 4,05 +/- 0,15 |
| Braid construction 16 x 7x (0,12+0,003/-0,003) | min. 84% | |
| Elongation at break for every wire | min 6% | |
| Tensile strength for every wire | 190N/mm2 | |
| Sheath | PVC - NO BAD ODORS | 6.15 +/-0.20 |
| Sheath color BLACK RAL 9005 | Thickness 0,8±0.1 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa （TM2） | |
| Tensile strength after 168 H at 80 ºc | +/-20%（TM2） | |
| Elongation at break | min. 150 %（TM2） | |
| Elongation at break after 168 H at 80 ºC | +/-20% （TM2） | |
| Bending test at low temperature | -15°C | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| Sheath marking | ||
| Delivery form | ||
| 2. Cable environmental characteristics | |||
| Environmental Space | Indoor | Outdoor | ||
| Working temperature | -20 ºC +75 ºC | ||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | |
| Flame Test Listing | vertical flame | IEC 60332-1-2 | |
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | |
| 3.- ELECTRICAL CHARACTERISTICS | |||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | |||
| Inner conductor resistance | Ohmios /km max. 65 | ||
| Outer conductor resistance | Ohmios /km max. 42 | ||
| Max. Loop current | Ampers 8 a 20 ºC - 5 a 40 ºC | ||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | ||
| Insulation resistance | Mohm x km > 5000 Mohm x km | ||
| Mutual capacitance | 67±2nF/km | ||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | ||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | |||
| Velocity of propagation | % | 66 | |
| Characteristic impedance | Ohmios | 75 +/- 3 | |
| Nominal Delay | nS/m max. | 5,1 | |
| MHz | dB/100m NOM | ||
| 50 | 8.5 | ||
| 100 | 11.8 | ||
| 200 | 16.5 | ||
| 450 | 26 | ||
| 800 | 35.8 | ||
| 800 | 35.8 | ||
| 1000 | 39.5 | ||
| Return Loss | 5 MHz - 1000 MHz | min. 20dB | |
| 1.- CABLE CONSTRUCTION | ||
| Inner conductor | Bare Copper | 0.58 +/-0.01 |
| Elongation at break | min 20% | |
| Adherence to dielectric | 22 -89 N | |
| Dielectric | polyethylene | 3.70 +/-0.05 |
| Dielectric constant of base PE 2,25 | ||
| Dielectric strength 1of PE 18 kV/mm | ||
| PE Oxidative Induction Time | min. 30 minutes / ASTM D 4565 Chapter 17 | |
| PE Oxidative Induction Time | min. 70% after 14 days / 90 ºC | |
| First screen | Copper Clad Aluminium Wire Braid | 4,05 +/- 0,15 |
| Braid construction 16 x 7x (0,12+0,003/-0,003) | min. 84% | |
| Elongation at break for every wire | min 6% | |
| Tensile strength for every wire | 190N/mm2 | |
| Power cord | Bare Copper 24*0.20±0.02mm+1.80mm PVC BLACK | 0.75mm2 |
| Bare Copper 24*0.20±0.01mm+ 1.80mm PVC RED | 0.75mm2 | |
| Power cord Out Sheath | PVC - NO BAD ODORS | 4.80±3.0mm |
| Sheath color BLACK RAL 9005 | Thickness min. 0,5mm | |
| Jacket thickness excentricity | max. 43 % | |
| Sheath | PVC - NO BAD ODORS | 6.15 +/-0.20 |
| Sheath color BLACK RAL 9005 | Thickness 0,8±0.1 mm | |
| Jacket thickness excentricity | max. 43 % | |
| Tensile strength | min .11MPa（TM2） | |
| Tensile strength after 168 H at 80 ºc | +/-20% （TM2） | |
| Elongation at break | min. 150 %（TM2） | |
| Elongation at break after 168 H at 80 ºC | +/-20%（TM2） | |
| Bending test at low temperature | -15°C | |
| Spark test | min. 2,5 kVrms | |
| Jacket shrinkage (ANSI/SCTE 88/2003) | max. 10 mm / sample 150 mm | |
| 2. Cable environmental characteristics | |||
| Environmental Space | Indoor | Outdoor | ||
| Working temperature | -20 ºC +75 ºC | ||
| CPR Cable Classifications | Euro Class Eca | EN50575: 2014+ A1:2016 | |
| Flame Test Listing | vertical flame | IEC 60332-1-2 | |
| UV Resistance per UL 1581, Paragraph 1200 |
Percent Retention of Tensile Strength & Elongation after 720 hours exposure shall be ≥ 80. |
UL2556 | |
| 3.- ELECTRICAL CHARACTERISTICS | |||
| 3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC | |||
| Inner conductor resistance | Ohmios /km max. 65 | ||
| Outer conductor resistance | Ohmios /km max. 42 | ||
| Max. Loop current | Ampers 8 a 20 ºC - 5 a 40 ºC | ||
| Dielectric strength | 2 kV D.C. or 1,5 kV A.C. for 1 min. | ||
| Insulation resistance | Mohm x km > 5000 Mohm x km | ||
| Mutual capacitance | 67±2nF/km | ||
| Voltage test of sheath | 2,5 kV A.C. or 3,75 kV D.C. for 1 min. | ||
| 3.2 Electrical characteristics - High frecuency - @ 20 ºC | |||
| Velocity of propagation | % | 66 | |
| Characteristic impedance | Ohmios | 75 +/- 3 | |
| Nominal Delay | nS/m max. | 5,1 | |
| MHz | dB/100m NOM | ||
| 50 | 8.5 | ||
| 100 | 11.8 | ||
| 200 | 16.5 | ||
| 450 | 26 | ||
| 800 | 35.8 | ||
| 800 | 35.8 | ||
| 1000 | 39.5 | ||
| Return Loss | 5 MHz - 1000 MHz | min. 20dB | |
Certifications
Product List
Contact Us
Add:No.1058 Jinxi Road,Linglong Industial Zone ,Lin'an City, Zhejiang Province,China.
Tel:+86 571 63761139
Fax:+86 571 63929811
E-mail: amanda@sanyuancable.com.cn
Mobile Phone Version
Sweep into the mobile version