KX6+2C OVERALL

KX6+2C OVERALL

KX6+2C OVERALL Specificatrion

CPR CLASS Eca

 

1.- CABLE CONSTRUCTION
Inner conductor Bare Copper 7*0.20 +/-0.01
Elongation at break min 20%
Adherence to dielectric 22 -89 N
Dielectric polyethylene  3.70 +/-0.05
Dielectric constant of base PE 2,25  
Dielectric strength 1of PE 18 kV/mm  
PE Oxidative Induction Time min. 30 minutes / ASTM D 4565 Chapter 17
PE Oxidative Induction Time min. 70% after 14 days / 90 ºC
First screen Copper Clad Aluminium Wire Braid 4,05 +/- 0,15
Braid construction 16 x 7x (0,12+0,003/-0,003)  min. 84%
Elongation at break for every wire min 6%
Tensile strength for every wire  190N/mm2
Inner Sheath PVC  - NO BAD ODORS 6.15 +/-0.20
Sheath color BLACK RAL 9005 Thickness  0,8±0.1 mm
Jacket thickness excentricity  max. 43 % 
Tensile strength  min .11MPa (TM2)
Tensile strength after 168 H at 80 ºc +/-20% (TM2)
Elongation at break  min. 150 %(TM2)
Elongation at break after 168 H at 80 ºC +/-20% (TM2)
Bending test at low temperature -15°C
Spark test  min. 2,5 kVrms
Jacket shrinkage (ANSI/SCTE 88/2003) max. 10 mm / sample 150 mm
Power cord Bare Copper 24*0.20±0.02mm+1.80mm PVC BLACK 0.75mm2
Bare Copper 24*0.20±0.01mm+ 1.80mm PVC RED 0.75mm2
Outer Sheath PVC  - NO BAD ODORS 10.0 +/-0.30
Sheath color BLACK RAL 9005 Thickness  1,0±0.2 mm
Jacket thickness excentricity  max. 43 % 
Tensile strength  min .11MPa  (TM2)
Tensile strength after 168 H at 80 ºc +/-20%(TM2)
Elongation at break  min. 150 %(TM2)
Elongation at break after 168 H at 80 ºC +/-20% (TM2)
Bending test at low temperature -15°C
Spark test  min. 2,5 kVrms
Jacket shrinkage (ANSI/SCTE 88/2003) max. 10 mm / sample 150 mm

 

2. Cable environmental characteristics
Environmental Space Indoor | Outdoor  
Working temperature                                -20 ºC +75 ºC  
CPR Cable Classifications Euro Class Eca EN50575: 2014+ A1:2016
Flame Test Listing                                                                      vertical flame IEC 60332-1-2
UV Resistance per UL 1581, Paragraph 1200

Percent Retention of Tensile Strength & 

Elongation after 720 hours 

exposure shall be ≥ 80.

UL2556

 

3.- ELECTRICAL CHARACTERISTICS
3.1 Electrical characteristics - DC and Low frecuency - @ 20 ºC
Inner conductor resistance  Ohmios /km max. 65
Outer conductor resistance  Ohmios /km max. 42
Max. Loop current  Ampers 8 a 20 ºC - 5 a 40 ºC
Dielectric strength  2 kV D.C. or 1,5 kV A.C. for 1 min.
Insulation resistance  Mohm x km > 5000 Mohm x km
Mutual capacitance  67±2nF/km
Voltage test of sheath  2,5 kV A.C. or 3,75 kV D.C. for 1 min.
3.2 Electrical characteristics - High frecuency - @ 20 ºC
Velocity of propagation  % 66
Characteristic impedance Ohmios 75 +/- 3
Nominal Delay nS/m max.  5,1
MHz dB/100m  NOM
50 8.5
100 11.8
200 16.5
450 26
800 35.8
800 35.8
1000 39.5
Return Loss  5 MHz - 1000 MHz  min. 20dB